An electronic grade epoxy that combines moderate curing rate and high conductivity with ease of use. It has a convenient 1-to-1 ratio, a workable ten minutes pot life, and a moderate curing rate. It achieves an operational level in five hours at room temperature. With heat, the 8330 cures in less than 15 minutes and maximizes its conductivity. čítajte viac
Modifikácií
tovar | |
|---|---|
3D Printer Filaments 1.75mm. 0.50 kg spool - HIP17WH5 | |
3D Printer Filaments 3.00mm. 0.50 kg spool - HIP30WH5 |
tovar | Artikel | Náklady | Objednať | |
|---|---|---|---|---|
3D Printer Filaments 1.75mm. 0.50 kg spool - HIP17WH5 | €18.07 | |||
3D Printer Filaments 3.00mm. 0.50 kg spool - HIP30WH5 | €18.07 |
Opís
High Impact Polystyrene. Used to make support structures that can also be dissolved in d-limonene without affecting the PLA object being printed. Print temperature: approximately 223°C. Print bed temperature: approximately 115°C (239°F).
Features & Benefits
- High Impact Polystyrene
- 1.75mm and 3.0mm diameters
- Low Diameter variance
- 0.50 KG spools
Vlastnosti
| Quality Control | Small Diameter | Big Diameter |
|---|---|---|
| Appearance | Off white | Off white |
| Specific Gravity | ISO 1183 @23 °C | 1.05 g/cm3 |
| Diameter Tolerance | 1.75 mm ±0.10 mm | 3.00 mm ±0.10 mm |
| Round Tolerance | ±0.05 mm | ±0.05 mm |
| UL Flammability Rating | UL-94 HB | UL-94 HB |
| Physical Properties | Method | Value |
| Ball Indentation Hardness | ISO 2039-1 | 90 N/mm2 [13 000 lb/in2] |
| Tensile Strength | ISO 527 | 27 MPa [3 900 lb/in2] |
| % Elongation | " | 64% |
| Flexural Strength | ISO 178 | 40 MPa [5 800 lb/in2] |
| Flexural Modulus | " | 1.6 MPa [230 000 lb/in2] |
| Izod Impact Strength | ISO 180/1A (notched) | 7 kJ/m2 |
| Charpy Impact Strength | ISO 179 (notched) | 8 kJ/m2 |
| Thermal Properties | Method | Value |
| Melt Flow Index | ISO 1133 @200 °C, 5 kg load | 5.5 mL per 10 min |
| Vicat Softening Temperature | ISO 306 @50 °C/h, 1 kg load | 100 °C [212 °F] |
| Heat Distortion Temperature | ISO 75 @1.8 MPa Unannealed | 78 °C [172 °F] |
| ISO 75 @1.8 MPa Annealed | 94 °C [201 °F] | |
| Working Temperature | - | 220—230 °C [428–446 °F] |
| Bed Temperature | - | 50–60 °C [122–140 °F] |