Zloženie špeciálne vyvinuté pre rýchle spájanie gumy, plastu, kovu a keramiky, má výbornú priľnavosť. čítajte viac
Modifikácií
tovar | |
---|---|
Kyanakrylátové Super lepidlo, tekutina, 20g - 8333-20G | |
Kyanakrylátové Super lepidlo, tekutina, 3g - 8333-3G |
tovar | Artikel | Náklady | Objednať | |
---|---|---|---|---|
Kyanakrylátové Super lepidlo, tekutina, 20g - 8333-20G | €0 | |||
Kyanakrylátové Super lepidlo, tekutina, 3g - 8333-3G | €0 |
Opís
Tento kyanoakrylátové Super lepidlo určené pre rýchle spájanie plastov, kovov a keramiky. Ukazuje vysoký výkon väzby. Lepidlo k dispozícii v demonštračných balíčkach, ako aj vo forme gélu 8334.
Vlastnosti
Storage | ||
---|---|---|
Store between 5 °C to 22 °C [41 and 72 °F] in dry area away from sunlight. | ||
Curing & Work Schedule | Value | |
Typical Handling Time a) | 10 s | |
Service Cure a,b) @22 °C [72 °F] | >24 h | |
Cure Type | Humidity | |
Shelf Life | 2 y | |
a) Assumes 50% relative humidity. b) As well as humidity, the type of material being bonded, bond gap, and temperature, may change the cure time. | ||
Temperature Service Range | Value | |
Constant Service Temperature | -55 °C to 80 °C [-67 °F to 176 °C] | |
Storage Temperature of Unmixed Parts | 5 °C to 22 °C [41 °F to 72 °F] | |
Physical Properties | Method | Value |
Color | Visual | Clear |
Density @25 °C [79 °C] | 1.05g/cm3 | |
Lap Shear Strength | ISO 4587 b) | |
Lap Shear Strength (Stainless Steel) | <20 s fixture time | >14.5 N/mm2 [>2 100 lb/in2] |
Lap Shear Strength (Aluminum) | <15 s fixture time | >12.1 N/mm2 [>1 750 lb/in2] |
Lap Shear Strength (ABS) | <10 s fixture time | >6.2 N/mm2 [>900 lb/in2] |
Lap Shear Strength (PVC) | <5 s fixture time | >6.2 N/mm2 [>900 lb/in2] |
Lap Shear Strength (Polycarbonate) | <30 s fixture time | >6.2 N/mm2 [>900 lb/in2] |
Lap Shear Strength (Phenolic Rubber) | <10 s fixture time | >6.2 N/mm2 [>900 lb/in2] |
Lap Shear Strength (Neoprene) | <5 s fixture time | >5.2 N/mm2 [>750 lb/in2] |
Butt Joints Tensile Strength (Stainless Steel) | ISO 6922 | >12.4 N/mm2 [>1 800 lb/in2] |
Electric Properties | Method | Value |
Volume Resistivity | ASTM D 257 | ≥2 × 1015 Ω·cm |
Dielectric Dissipation & Constant | dissipation D, constant, k’ | |
Dissipation & Constant @1 kHz | ASTM D 150-98 | 0.02 2 to3.5 |
Note: Specifications are for sample cured at 50% relative humidity for at least 24 hours.
a) N/mm2 = MPa; lb/in2 = psi b) The fixture time is the time required to develop a shear strength of 0.1 N/mm2. This corresponds to the strength at which the parts may no longer be moved independently. |
Materials Subject to Bonding | |||
---|---|---|---|
Natural | Plastics/Polymers | Ceramics | Metals |
Latex Leather Paper, Fiber Fabric Rubber Wood |
ABS Acrylic Bakelite EPDM Fiberglass NBR (Nitrile rubber) Neoprene Nitrile Phenolic Polybutylene Terephthalate Polycarbonate Polyester PVC Styrene-Butadiene rubber | Porcelain |
Aluminum Brass Chrome Copper Steel
|
Note: The MG 8333 Super Glue is not compatible with contaminants like oil, and greases that may affect adhesion. If contamination is present, clean the surface with a suitable cleaner such as MG Chemicals 4050 Safety Wash, 406B Superwash, or 824 Isopropyl Alcohol. |
Retained Adhesive Strength and After Chemical/Solvent Exposur | |||
---|---|---|---|
Chemical/Solvet | Conditions/Temperature (°C) | Exposure Duration (hour) | Percent of Initial Strength |
Gasoline Isopropanol Ethanol Freon Motor Oil Polycarbonate |
22 °C 22 °C 22 °C 22 °C 40 °C 40 °C @95% RH |
500 500 500 500 500 500 |
100% 100% 100% 100% 100% 100% |
Chemical Resistance — To test the chemical resistance, the adhesive was aged in various chemicals and the strength of the adhesive bond was compared to that of control specimens. |